- Specifications: 0.10 +.08/-.05% from 2.0µ to 14µ
- Parallelism: < 10 arc minutes
- Size: 25.0 Ø +0.0 / -0.2
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 90% of OD
- Flatness: 1 or better at of Interest
- Substrate: Ge
- %T (Optical Density): -
- Specifications: 0.1% +0.08/-0.05% from 5200nm - 7000nm , A/R 1.0% Rx (avg) from 5200nm - 7000nm
- Parallelism: <10 arc min
- Size: 25.0 Ø +0.0 / -0.2
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 90% of OD
- Flatness: <= 1 waves at 5800nm
- Substrate: Ge
- %T (Optical Density): -
- Specifications: 0.10 +.08/-.05% from 2.0µ to 14µ
- Parallelism: < 10 arc minutes
- Size: 50.0 Ø +0.0 / -0.2
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 90% of OD
- Flatness: 1 or better at of Interest
- Substrate: Ge
- %T (Optical Density): -
- Specifications: 0.1% +0.08/-0.05% from 5200nm - 7000nm , A/R 1.0% Rx (avg) from 5200nm - 7000nm
- Parallelism: <10 arc min
- Size: 50.0 Ø +0.0 / -0.2
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 90% of OD
- Flatness: <= 1 waves at 5800nm
- Substrate: Ge
- %T (Optical Density): -
- Wavelength: 325.0 ±5.0
- Operating Temperature: 23.0
- Parallelism: Commercial
- Transmission: 85%
- Blocking: >OD3 avg from 0.9 X 50% pt. to 200nm
- Size: 12.5 Ø +0 / -0.2
- Thickness: 3.3 ±0.25
- Scratch-Dig: 80/50
- Clear Aperture: 95%
- Flatness: Commercial
- Angle of Incidence: 0
- 50% Cut-on Wavelength: 325.0
- Wavelength: 325.0 ±5
- Operating Temperature: 23.0
- Parallelism: Commercial
- Transmission: 85%
- Blocking: >OD3 avg from 0.9 X 50% pt. to 200nm
- Size: 25.0 Ø +0 / -0.5
- Thickness: 3.3 ±0.25
- Scratch-Dig: 80/50
- Clear Aperture: 95%
- Flatness: Commercial
- Angle of Incidence: 0
- 50% Cut-on Wavelength: 325.0
- Wavelength: 325.0 ±5
- Operating Temperature: 23.0
- Parallelism: Commercial
- Transmission: 85%
- Blocking: >OD3 avg from 0.9 X 50% pt. to 200nm
- Size: 50.0 Ø +0 / -0.5
- Thickness: 3.3 ±0.25
- Scratch-Dig: 80/50
- Clear Aperture: 95%
- Flatness: Commercial
- Angle of Incidence: 0
- 50% Cut-on Wavelength: 325.0
- Wavelength: 325.0 ±5
- Operating Temperature: 23.0
- Parallelism: Commercial
- Transmission: 85%
- Blocking: >OD3 avg from 0.9 X 50% pt. to 200nm
- Size: 50.0 x 50.0 +0 / -0.5
- Thickness: 3.3 ±0.25
- Scratch-Dig: 80/50
- Clear Aperture: 95%
- Flatness: Commercial
- Angle of Incidence: 0
- 50% Cut-on Wavelength: 325.0
- Wavelength: 334 ±2
- Emission Line: N/A
- Operating Temperature: 23
- Parallelism: Commercial
- Bandwidth (FWHM): 10.0 ±2 nm
- Minimum Transmission: 90%
- Blocking: 1x10-4 avg. 200-1200nm
- Size: 25.0 Ø +0 / -0.1
- Thickness: 5.0 ±0.25
- Scratch-Dig: 80/50
- Clear Aperture: 21mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Filter Type: 3
- Wavelength: 3030 ±30
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 850 ±50 nm
- Minimum Transmission: >85% avg.
- Blocking: 1x10-3 avg. 300nm to 7,500nm
- Size: 0.995 Ø ±0.005
- Thickness: 0.040 ±.004
- Scratch-Dig: 80/50
- Clear Aperture: 23mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Silicon
- Gas: N/A
- Wavelength: 3040 ±20
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 105 ±10 nm
- Minimum Transmission: 75%
- Blocking: 1x10-3 avg. X-Ray to 30µ
- Size: 25.0 Ø +0 / -0.25
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 21mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Sapphire
- Gas: Methanol and Ethanol
- Wavelength: 3075 ±20
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 105 ±10 nm
- Minimum Transmission: 75%
- Blocking: 1x10-3 avg. X-Ray to 30µm
- Size: 25.0 Ø +0 / -0.25
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 21mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Sapphire
- Gas: Methanol and Ethanol
- Wavelength: 3100 ±30
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 950 ±50 nm
- Minimum Transmission: >85% avg.
- Blocking: 1x10-3 avg. 300nm to 7,500nm
- Size: 0.995 Ø ±0.005
- Thickness: 0.040 ±nom
- Scratch-Dig: 80/50
- Clear Aperture: 23mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Silicon
- Gas: N/A
- Wavelength: 3100 ±75
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 1300 ±100 nm
- Minimum Transmission: 85%
- Blocking: 1x10-3 avg. X-Ray to 5500nm
- Size: 25.0 Ø ±0.1
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 22mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Germanium
- Gas: N/A
- Wavelength: 3100 ±75
- Emission Line: N/A
- Operating Temperature: 23
- Parallelism: Commercial
- Bandwidth (FWHM): 1300 ±100 nm
- Minimum Transmission: 85%
- Blocking: 1x10-3 avg. X-Ray to 5,450nm
- Size: 50.0 Ø ±0.1
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: N/A
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Germanium
- Gas: N/A
- Wavelength: 3150 ±nom
- Operating Temperature: 23.0
- Parallelism: 3 arc minutes or better
- Transmission: 92%
- Blocking: 1600nm to 3100nm > OD3 (avg)
- Size: 12.5 Ø ±0.1
- Thickness: 0.5 ±0.03
- Scratch-Dig: 80/50
- Clear Aperture: 11mm Ø min
- Flatness: TWF: < 2.0 @ 633nm
- Substrate: Silicon
- Angle of Incidence: 0 cone
- 5% Wavelength: N/A
- Wavelength: 3150 ±nom
- Operating Temperature: 23.0
- Parallelism: 3 arc minutes or better
- Transmission: 92%
- Blocking: 1600nm to 3100nm > OD3 (avg)
- Size: 10.0 Ø ±0.1
- Thickness: 0.5 ±0.03
- Scratch-Dig: 80/50
- Clear Aperture: 9mm Ø min
- Flatness: TWF: < 2.0 @ 633nm
- Substrate: Silicon
- Angle of Incidence: 0
- 5% Wavelength: N/A
- Wavelength: 3200 ±50
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 900 ±50 nm
- Minimum Transmission: >90% avg.
- Blocking: 1x10-3 avg. 300nm to 8,000nm
- Size: 0.995 Ø ±0.005
- Thickness: 0.040 ±nom
- Scratch-Dig: 80/50
- Clear Aperture: 22mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Silicon
- Gas: N/A
- Wavelength: 3283.0 ±40
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 135.0 ±30 nm
- Minimum Transmission: 75%
- Blocking: OD3 avg. from UV-30um
- Size: 25.0 Ø +0 / -0.25
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 22mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Sapphire
- Gas: N/A
- Wavelength: 3370 ±30
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 120 ±30 nm
- Minimum Transmission: 83%
- Blocking: 1x10-3 avg. X-Ray to 30µ
- Size: 25.0 Ø +0 / -0.25
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 22mm Ø min
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Sapphire
- Gas: N/A
- Wavelength: 3375 ±20
- Emission Line: N/A
- Operating Temperature: 23.0
- Parallelism: Commercial
- Bandwidth (FWHM): 200 ±20 nm
- Minimum Transmission: 80%
- Blocking: >OD2.5 avg. X-Ray to 30um
- Size: 12.5 +0.0 / -0.2
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 11mm
- Flatness: Commercial
- Effective Refractive Index: N/A
- Substrate: Sapphire
- Gas: N/A
- Wavelength: 3400 ±140
- Operating Temperature: 23.0
- Parallelism: Commercial
- Transmission: 90%
- Blocking: 1x10-3 avg. X-Ray to 3200
- Size: 25.0 Ø +0 / -0.1
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 21mm Ø min
- Flatness: Commercial
- Substrate: Germanium
- Angle of Incidence: 0
- 5% Wavelength: N/A
- Wavelength: 3400 ±140
- Operating Temperature: 23
- Parallelism: Commercial
- Transmission: 90%
- Blocking: <0.1% avg X-ray to 3200
- Size: 25.0 Ø +0 / -0.2
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 22mm Ø min
- Flatness: Commercial
- Substrate: Germanium
- Angle of Incidence: 0
- 5% Wavelength: N/A
- Wavelength: 3400 ±140
- Operating Temperature: 23
- Parallelism: Commercial
- Transmission: 90%
- Blocking: <0.1% avg x-ray to 3200nm
- Size: 50 +0 / -0.2
- Thickness: 1.0 ±0.2
- Scratch-Dig: 80/50
- Clear Aperture: 45mm Ø min
- Flatness: Commercial
- Substrate: Germanium
- Angle of Incidence: 0
- 5% Wavelength: N/A
PART NO.
DESCRIPTION
1 - 5 pcs.
6 - 10 pcs.
> 10 pcs.
Stock Status
$453.00
$385.00
$340.00
In Stock
$552.00
$469.00
$414.00
In Stock
$934.00
$794.00
$701.00
In Stock
$1,023.00
$870.00
$767.00
In Stock
$81.00
$70.00
$62.00
In Stock
$123.00
$106.00
$93.00
In Stock
$167.00
$144.00
$127.00
In Stock
$199.00
$171.00
$151.00
In Stock
$219.00
$208.00
$197.00
In Stock
$325.00
$325.00
$325.00
In Stock: 7
$270.00
$270.00
$270.00
In Stock: 10
$270.00
$270.00
$270.00
In Stock: 13
$325.00
$325.00
$325.00
In Stock: 7
$183.00
$183.00
$183.00
In Stock: 38
$247.00
$247.00
$247.00
In Stock: 2
$195.00
$195.00
$195.00
In Stock: 24
$195.00
$195.00
$195.00
In Stock: 103
$345.00
$345.00
$345.00
In Stock: 10
$460.00
$460.00
$460.00
In Stock: 34
$270.00
$270.00
$270.00
In Stock: 2
$180.00
$180.00
$180.00
In Stock: 14
$207.00
$207.00
$207.00
In Stock: 10
$207.00
$207.00
$207.00
In Stock: 15
$328.00
$328.00
$328.00
In Stock: 4